Residual stress measurements on a stress relieved Zircaloy-4 weld by neutron diffraction

The macroscopic stress distribution across an annealed Zircaloy-4 gas tungsten arc weld was measured by neutron time-of-flight diffraction at the SMARTS diffractometer at Los Alamos National Laboratory. The stresses after annealing are about 40% lower than those in the same weld prior to heat treatment. The intergranular strains in the reference coupons, which give the macroscopic stress free lattice spacings, are consistent with the difference in cooling the strongly textured plate and the weakly textured weld.