Tensile properties of ferritic/martensitic steels irradiated in STIP-I

Specimens of ferritic/martensitic (FM) steels T91, F82H, Optimax-A and the electron beam weld (EBW) of F82H were irradiated in the Swiss spallation neutron source (SINQ) Target-3 in a temperature range of 90–370 °C to displacement doses between 3 and 12 dpa. Tensile tests were performed at room temperature and the irradiation temperatures. The tensile test results demonstrated that the irradiation hardening increased with dose up to about 10 dpa. Meanwhile, the uniform elongation decreased to less than 1%, while the total elongation remained greater than 5%, except for an F82H specimen of 9.8 dpa tested at room temperature, which failed in elastic deformation regime. At higher doses of 11–12 dpa, the ductility of some specimens recovered, which could be due to the annealing effect of a short period of high temperature excursion. The results do not show significant differences in tensile properties for the different FM steels in the present irradiation conditions.