Pressure-induced crystallization in a bulk amorphous Zr-based alloy

Crystallization of multi-component on amorphous Zr-based alloy (Zr41Ti14Cu12.5Ni9Be22.5C1) is investigated at different pressures and temperatures. We have previously found that the primary crystallization temperature decreases with increasing pressure below 6 GPa, and the crystallization follows a different process under high pressure when compared to that at ambient pressure. In this work, pressure-induced crystallization is observed by in situ X-ray diffraction (XRD) using synchrotron radiation in a diamond anvil cell at ∼25 GPa and room temperature. This phase transition between amorphous and crystalline is reversible and the crystallized sample returns to the amorphous state during decompression. The mechanism for pressure-induced crystallization is discussed. We suggest that the crystallized phases under high pressure are interstitial solid solution phases formed from the amorphous matrix without long-range atomic rearrangements.