Formation of silica/epoxy hybrid network polymers

Epoxy-based inorganic–organic hybrid polymers, for use as a matrix in coatings, have been prepared from 3-glycidoxypropyltrimethoxysilane by a sol–gel process. The precursor molecule possesses both epoxy and silicon alkoxide functionality and so interlinked inorganic–organic networks can be formed. Diethylenetriamine was used to open the epoxy rings and form the organic network to an extent determined by the initial ratio of amine to epoxy groups. The materials were cured either at room temperature or with an additional heat treatment at 150 °C. Structural characterisation of the cured hybrid materials was performed using a combination of Raman, and 29Si and 13C MAS NMR spectroscopies. These show that the formation of the two networks does not occur independently and the rate or extent of organic cross-linking has a direct effect on the extent of the inorganic network formation, and vice-versa.