Crystallization behavior of Zr41Ti14Cu12.5Ni10Be22.5 bulk metallic glass under the action of high-density pulsing current

The crystallization behavior of Zr41Ti14Cu12.5Ni10Be22.5 bulk metallic glass (Vit1 BMG) under the action of high-density pulsing current (HDPC) have been studied experimentally. It has been found that high-density pulsing current can directly induce the rapid nanocrystallization of Vit1 BMG. The multiple crystallization processes of Vit1 BMG induced by HDPC have been confirmed as Amorphous → Amorphous + i-phase → Be2Zr + Zr2Cu + Ni7Zr2 + FCC phase + other phases → Zr2Cu + Ni7Zr2 + FCC phase + other phases. By comparing to the crystallization behavior of Vit1 BMG induced by isothermal annealing, the crystallization temperature is reduced and crystallizing process is significantly shortened, while the sequence of crystallization process in both cases is basically same. The present results show that the HDPC has significantly influenced the crystallizing kinetics of Vit1 BMG due to that it can greatly promote the movement and rearrangement of atoms, which will result in a rapid nanocrystallization. It suggests that HDPC treatment can be an effective way to induce the rapid nanocrystallization of BMGs.