Sol–gel synthesis of erbium-doped yttrium silicate glass–ceramics

Yttrium silicate glasses and glass–ceramics were prepared by the sol–gel process. Yttrium nitrate was added to tetraethyl orthosilicate in amounts representing between 0.2 and 20 mol%, as well as amounts corresponding to the disilicate composition. Some samples were doped with erbium acetate. The solutions underwent gellation in 2–7 days and were dried for 2 weeks. Differential thermal analysis was used to design a multi-step heat treatment to 1000 °C to densify samples to transparent or translucent monoliths. Above 1000 °C, samples crystallized to yttrium disilicate and cristobalite. Phase separation before crystallization influenced the formation of the crystal phases.