Glass formation ability and mechanical properties of Ti40Cu40Zr10Ni10 alloy

Melt-spun ribbon and bulk samples in cylindrical rod form with diameter ranging from 2 mm to 4 mm of Ti40Cu40Zr10Ni10 alloy were prepared by melt-spinning technique and copper mould casting method, respectively. The microstructure, thermal stability and mechanical properties of the bulk samples were investigated. A completely glassy single phase is formed in the 2 mm rod sample. Increasing the diameter of the rod samples resulted in the formation of CuTi crystalline phase in the 3 mm and 4 mm rod samples. The 2 mm single glassy rod sample exhibited a large supercooled liquid region ΔTx = 58 K and γ = Tx/(Tg + Tl) is 0.390, which indicated that the alloy possessed a good glass-forming ability. The bulk samples also exhibited good mechanical properties. The 2 mm rod sample showed the highest yield strength of about 2086 MPa. The 3 mm rod sample not only showed high yield strength of about 2000 MPa, but also enhanced plastic strain of about 0.71%.