Correlation of boron content and high temperature stability in Si–B–C–N ceramics

The preparation and characterization of precursor derived Si–B–C–N ceramics with similar Si/C/N ratios but variable boron content are reported. The polymeric precursors were prepared via hydroboration of poly(methylvinylsilazane) using different BH3·SMe2/polymer stoichiometries. High temperature thermogravimetric analysis of as-pyrolysed ceramics as well as XRD studies of post-annealed samples display a retarding effect of boron on both crystallization of SiC and Si3N4 and stabilization of crystalline β-Si3N4.