Influence of zeolites on the sintering and technological properties of porcelain stoneware tiles

Low-cost zeolitic rocks are promising substitutes for feldspathic fluxes in ceramic bodies, since their fusibility, modest hardness and high cation exchange capacity (CEC) should improve grinding and sintering. Five large-scale Italian deposits of natural zeolites with different mineralogy were characterised and tested in porcelain stoneware bodies. Their behaviour during processing was appraised and compared with that of zeolite-free bodies. Zeolites increased the slip viscosity during wet grinding, causing a coarser grain size distribution and consequently some drawbacks in both unfired and fired tiles. After overcoming this hindrance by dry grinding of zeolite rocks, the technological behaviour of zeolite-bearing tiles appear to be similar to that of current porcelain stoneware, though with larger firing shrinkage and residual closed porosity.