Aqueous tape casting processing of low dielectric constant cordierite-based glass-ceramics—selection of binder

In this paper, four different binders were investigated in the process of aqueous tape casting of cordierite-based glass-ceramics and their effects on the rheological behaviour of the suspensions and on the microstructures of the green tapes were compared. Meanwhile, a good compatibility between the dispersant and binder was found to be a predominant factor to obtain an optimised cordierite glass-ceramic tape. The microstructure of the green tape was observed by SEM and the weight loss during binder burn out process was determined by DTA/TG. The dielectric constant and dielectric loss of the sintered tapes (at 1150 °C for 2 h) was also measured.