Reinforcement of precursor-derived Si–C–N ceramics with carbon nanotubes

Nanocomposites consisting of precursor-derived Si–C–N ceramics incorporated with carbon nanotubes (CNTs) were successfully prepared by casting of a mixture of CNTs and a liquid precursor polymer followed by cross-linking and thermolysis. The effect of CNTs on the fracture toughness of these nanocomposites was investigated by a thermal loading technique. The results reveal a dependence of the fracture toughness on the type of the CNTs. One type shows a significant increase of the fracture toughness at CNT contents of only 1–2 mass%, whereas the other one exhibits no effect. The microstructural effects of CNTs observed at the fracture surfaces of the nanocomposites by scanning electron microscope (SEM) and transmission electron microscope (TEM) can be correlated with the observed fracture toughness behavior.