Comparison of fracture resistance as measured by the indentation fracture method and fracture toughness determined by the single-edge-precracked beam technique using silicon nitrides with different microstructures

Because of the industrial need for an assessment of fracture resistance, KR from small ceramic parts, KR of Si3N4 ceramics has been measured by the indentation fracture (IF) method using representative formulae to evaluate the compatibility with the fracture toughness, KIc determined from the single-edge-precracked beam (SEPB) technique. KR of the fine Si3N4 showed little dependence on the crack length, whereas the samples with coarse microstructures exhibited a rising R-curve behavior. The IF equation which gave the nearest value to KIc from SEPB was different depending on the microstructures. The assessment of fracture resistance with Miyoshiʹs equation was considered to be preferable for the flat R-curve behavior. By contrast, in the case of the rising R-curve behavior, it was revealed that the relationship between the IF and SEPB values was difficult to explain unless the effective crack extension against KIc for SEPB was clarified.