La-Si-O-N glasses: Part II: Vickers hardness and refractive index

Vickers hardness and refractive index have been determined for a series of La-Si-O-N oxy-nitride glasses containing 30–62 e/o of La and 9–68 e/o of N. The hardness varies between 7.7 and 11.5 GPa at a load of 1 kg and is dependent of the N content, while the La content does not influence it significantly. The increase of the hardness with N content is, contrary to reported findings for other oxy-nitride glasses, found not to be linear over the whole compositional range. The refractive index varies between 1.8 and 2.3 and increases non-linearly with increasing N content. The compositional variations of hardness and refractive index are compared with previously published results.