Nanoindentation of WC–Co hardmetals

WC–Co cemented carbide has been investigated using instrumented indentation with maximum applied loads from 0.1 to 10 mN. The hardness and indentation modulus of individual phases and the influence of crystallographic orientation of WC on the hardness and indentation modulus have been studied. The hardness of the Co binder was approximately 10 GPa and that of WC grains up to 50 GPa with relatively large scatter under the indentation load of 1 mN. Investigation of the role of crystallographic orientation of WC grains on hardness at 10 mN load revealed average values of HITbasal = 40.4 GPa (EITbasal = 674 GPa) and HITprismatic = 32.8 GPa (EItprismatic = 542 GPa), respectively. The scatter in the measured values at low indentation loads is caused by the effects of surface and sub-surface characteristics (residual stress, damaged region) and at higher loads by “mix-phase” volume below the indenter.