Effect of oxide nanofillers on fabrication, structure, and properties of zirconia-based composites

We have studied the effect of NiO on the sintering of yttria-stabilized zirconia at temperatures ranging from 1300 °C to 1500 °C in air and argon environments. It was found that the addition of NiO stabilized the cubic phase of ZrO2 independently from the sintering atmosphere. The monoclinic phase of ZrO2 formed only during sintering within the air environment at temperatures higher than 1450 °C. The transformation of NiO to Ni by reversible decomposition depends on the sintering atmosphere, and this can lead to variations in the nature of inclusions and in changes of the structure and properties of nanocomposite materials in the system ZrO2–NiO(Ni). NiO and Ni inclusions can increase the indentation fracture toughness of zirconia–nickel oxide composite material more than 50%, which can be compared with zirconia ceramics during sintering in a neutral atmosphere alone.