Wear behavior of low-cost, lightweight TiC/Ti–6Al–4V composite under fretting: Effectiveness of solid-film lubricant counterparts

The wear behavior of low-cost, lightweight 10 wt% titanium carbide (TiC)-particulate-reinforced Ti–6Al–4V matrix composite (TiC/Ti–6Al–4V) was examined under fretting at 296, 423, and 523 K in air. Bare 10 wt% TiC/Ti–6Al–4V hemispherical pins were used in contact with dispersed multiwalled carbon nanotubes (MWNTs), magnetron-sputtered diamond-like carbon/chromium (DLC/Cr), magnetron-sputtered graphite-like carbon/chromium (GLC/Cr), and magnetron-sputtered molybdenum disulfide/titanium (MoS2/Ti) deposited on Ti–6Al–4V, Ti–48Al–2Cr–2Nb, and nickel-based superalloy 718. When TiC/Ti–6Al–4V was brought into contact with bare Ti–6Al–4V, bare Ti–48Al–2Cr–2Nb, and bare nickel-based superalloy 718, strong adhesion, severe galling, and severe wear occurred. However, when TiC/Ti–6Al–4V was brought into contact with MWNT, DLC/Cr, GLC/Cr, and MoS2/Ti coatings, no galling occurred in the contact, and relatively minor wear was observed regardless of the coating. All the MWNT, DLC/Cr, GLC/Cr, and MoS2/Ti coatings on Ti–6Al–4V were effective from 296 to 523 K, but the effectiveness of the MWNT, DLC/Cr, GLC/Cr, and MoS2/Ti coatings decreased as temperature increased.