An experimental study on bending fretting fatigue characteristics of 316L austenitic stainless steel
Author/Authors
Peng، نويسنده , , J.F. and Song، نويسنده , , C. and Shen، نويسنده , , M.X. and Zheng، نويسنده , , J.F. and Zhou، نويسنده , , Z.R. and Zhu، نويسنده , , M.H.، نويسنده ,
Issue Information
ماهنامه با شماره پیاپی سال 2011
Pages
10
From page
1417
To page
1426
Abstract
Bending fretting fatigue tests of 316L austenitic stainless steel plates against 52100 steel cylinders have been carried out under same normal load and varied bending loads. Tests of plain bending fatigue were carried out as a control group. The S–N curves of the bending fatigue were made. The results indicated that there was an obvious drop of life under the condition of bending fretting fatigue due to higher local contact stress. A dislocation model of micro-crack nucleation mechanism, as a manner of zig-zag mode, was created to explain the nucleation of fretting fatigue cracks.
Keywords
microstructure , Dislocation model , Fretting damage , Bending Fretting fatigue