Thin polymer film based rapid surface acoustic wave humidity sensors

Polyvinyl alcohol (PVA) and polyvinyl pyrrolidone (PVP) thin films, deposited on the surface of glass slides, were studied using transmission FTIR spectroscopy upon varying relative humidity (RH) from 2 to 70%. The obtained data revealed fast dynamics of water vapor adsorption–desorption with responses on the order of several seconds. Based on the fast FTIR signal intensity changes versus RH, it was proposed that a similar rapid response can be achieved for PVA and PVP coated SAW devices due to changes in mass-loading and film viscoelastic properties upon absorption of water vapor in the films. Sub-micron thickness films were spin-coated onto the surface of LiNbO3 SAW substrates. Both PVA and PVP based humidity sensors revealed prompt reversible response to variations in humidity, although PVP-based device demonstrated better sensor parameters with total insertion loss variation of about 50 dB over the studied RH range and response time 1.5 s for the humidity step 5–95% (recovery time – 2.5 s), representing one of the fastest SAW-based humidity sensors reported to date.