Ethanol sensing using CuO/MWNT thin film

Copper (II) oxide (CuO)/multiwall carbon nanotube (MWNT) thin film based ethanol-sensors were fabricated by dispersing CVD-prepared MWNTs in varying concentration over DC magnetron sputtered-CuO films. The responses of these sensors as a function of MWNT concentrations and temperatures were measured, and compared. The sensing response was the maximum at an operating temperature near 400 °C for all the samples irrespective of the MWNTs dispersed over them. At optimum operating temperature (Topt) of 407 ± 1 °C, the response is linear for 100–700 ppm range and tends to saturate at higher concentrations. In comparison with bare CuO sample, the response of CuO/MWNT sensing films increased up to 50% in the linear range. The response improvement for 2500 ppm of ethanol was up to 90% compared to bare CuO sample. In addition, the sensing response time also reduced to around 23% for lowest ethanol concentration at Topt. However, a decrease in the sensor response was observed on films with very high concentrations of MWNTs.