Near-band-edge photoluminescnce in Cu(In,Ga)Se2 solar cells

Photoluminescence (PL) and PL decay characteristics of the near-band-edge (NBE) PL at room temperature have been studied on the Cu(In,Ga)Se2 (CIGS) solar cells. The carrier recombination process has been discussed with emphasis on the photovoltaic properties of the solar cell. It has been found that: (i) PL intensity of the CIGS solar cells is much stronger than that in the corresponding CIGS thin films, (ii) the PL decay time of the cell is longer than that of the CIGS film, and (iii) the PL decay time of the CIGS solar cell exhibits strong dependence on the PL excitation intensity. In the CIGS solar cell, intense PL is obtained under the open circuit condition (oc), in contrast to the very low PL yield under the short circuit (sc) condition. The PL decay time under the sc condition is much shorter than that under the oc condition. Excitation intensity dependence of PL intensity and the PL decay time have been studied, and they are discussed with relation to the photo-voltage due to the PL excitation light. PL and injection EL under the external DC bias have been studied. The mapping image of NBE-PL intensity has been compared with that of the laser beam induced current (LBIC), and the PL intensity image reflects the photovoltaic properties of the CIGS solar cells. We demonstrated that NBE-PL of the CIGS solar cell reflects the photovoltaic effect, and it can be utilized as a powerful characterization method.