Physical and mechanical properties of mortar using waste Polyethylene Terephthalate bottles

This paper studied the effects of aggregate gradation, sand-to-Polyethylene Terephthalate (PET) ratio, and curing conditions on physical and mechanical properties of recycled PET mortar. Infrared Spectrum test was performed to investigate the mechanism of strength development. Test results indicated that recycled PET mortar with continuously graded sand exhibited higher strength compared with mortar with single-sized gradation. As the sand-to-PET ratio increased, the compressive and flexural strength of recycled PET mortar increased. Compressive strength could reach 30 MPa within 3 h, which was over 90% of its 7-day strength. Samples cured under higher temperature had higher strength compared with specimens cured under low temperature. The curing time did not significantly influence the strength development. Infrared Spectrum test showed that more crystal was formed under higher curing temperature. This study reveals an innovative, easily implemented method to create a new mortar material by recycling waste PET bottles.