Determination of ultratrace impurity elements in high purity niobium materials by on-line matrix separation and direct injection/inductively coupled plasma mass spectrometry

The determination of 52 impurity elements in niobium materials (niobium metal, niobium oxide (V), and niobium pentaethoxide) was performed by inductively coupled plasma mass spectrometry (ICP-MS) with on-line anion exchange matrix separation as well as direct nebulization. Niobium material samples were decomposed with a mixture of hydrofluoric acid and nitric acid to prepare 10% niobium solutions. In the on-line anion exchange matrix separation/ICP-MS, the niobium and hydrofluoric acid concentrations in sample solution were adjusted to 5% and ca. 8 M, respectively. The solution was then injected into the carrier stream from the sample loop of injection valve to pass through an anion exchange resin column. In the anion exchange separation, niobium in the fluoro-complex form was adsorbed on the resin, while impurity elements were eluted. The eluted elements were introduced into ICP-MS for the determination of 25 impurity elements. On the other hand, 27 impurity elements could not be separated well from niobium matrix under the above anion exchange conditions, and then the sample solution with the niobium concentration of max. 0.2% containing internal standard elements was injected from the sample loop of injection valve directly to introduce into ICP-MS. As a result, 52 impurity elements in three kinds of niobium materials could be determined at the ng g−1 level.