Study on the preparation and properties of novolac epoxy/graphite composite bipolar plate for PEMFC

In this study, the graphite/polymer composite bipolar plate was manufactured by a bulk-molding compound process. Low-cost novolac epoxy was chosen to compound with natural graphite and black carbon. The electrical properties and mechanical properties of composite bipolar plate were studied. The aging behavior was characterized according to the changes in property before and after the immersion test. The results show that the composite bipolar plates have good corrosion resistibility in the simulated solution of 0.005 mol L−1 H2SO4 + 2 × 10−6 mol L−1 HF. TGA result shows that the novolac epoxy/NG composite has excellent thermal stability. The optimum processing conditions for preparing composite bipolar plate are: resin content about 15 wt.%; molding pressure 200 MPa; curing temperature 180 °C; graphite particle size −200 mesh. Under the optimum conditions, the composite bipolar plates have been produced, the electrical conductivity can attain to 120 S/cm and flexural strength is higher than 38 MPa.