The catalytic effect of Fe and Cr on hydrogen and deuterium absorption in Mg thin films

We examined the deuterium absorption and desorption of 55 nm thick Mg films alloyed with Fe and Cr using in-situ neutron reflectometry. The Mg alloy films were covered with bimetallic catalyst layers and could be fully absorbed at room temperature at a pressure of 8 mbar. The NR experiments revealed a deuterium gradient within the Mg alloy layers during absorption and a large deuterium uptake up to a D/M ratio of about 0.45 before the layer started to expand and form magnesium deuteride (MgD2). Our NR data suggest that the catalytic effect of the Fe–Cr alloy is based on the avoidance of the formation of a blocking MgD2 layer in the early stages of the absorption process leading to a fast hydrogen absorption kinetics.