A novel multielectrochromic copolymer based on 1-(4-nitrophenyl)-2,5-di(2-thienyl)-1H-pyrrole and EDOT

Copolymer of 1-(4-nitrophenyl)-2,5-di(2-thienyl)-1H-pyrrole (NTP) with 3,4-ethylene dioxythiophene (EDOT) was electrochemically synthesized and characterized. Resulting copolymer film has distinct electrochromic properties. It has five different colors (light red, red, light grey, green, and blue). At the neutral state λmax value due to the π–π∗ transition was found to be 550 nm and Eg was calculated as 1.6 eV. Double potential step chronoamperometry experiment shows that copolymer film has good stability, fast switching time (1.2 s) and high optical contrast (42%). ochromic device based on P(NTP-co-EDOT) and poly(3,4-ethylenedioxythiophene) was constructed and characterized. Oxidized state of the device shows light red color whereas reduced state blue color. At interval potentials device has good transparency and colors of the device are yellow and grey. Maximum contrast (T%) and switching time of the device were measured as 23% and 1.1 s at 650 nm. Electrochromic devices has good environmental and redox stability.