Influence of bimaterial interface on kinking behaviour of a crack growth emanating from notch

The mechanism of crack deviation by an interface modifies considerably the behaviour of bimaterials fracture. Their fracture resistance is highly affected by the difference of the elastic properties of the bonded materials. In this work, the finite element method is applied to analyze the behaviour of a crack emanating from semicircular notch root growing in interface ceramic/metal composites and perpendicularly to this interface. The obtained results showed that the crack grew to interface from harder material, its energy decreased at the approach of the interface, in this case was retarded; an inverse phenomenon occurs if the crack is propagated towards a lower strength material and its energy increases, it has tendency to accelerate. The effects of geometry on the crack deflection near the interface are also discussed.