LEED and STM studies of the stability of the MoO2(100) surface

Atomic scale images and low energy electron diffraction pattern of a MoO2(100) single crystal surface are presented, which show different structural modifications depending on surface preparation. A short in-situ heat treatment of the as-grown single crystal results in an atomically ordered surface whose diffraction pattern and STM images are consistent with those expected from the bulk structure. The symmetry of the STM images suggests an oxygen termination of the surface. A significantly longer heat treatment causes a thermodynamically stable (4 × 1) reconstruction which is interpreted to be due to a loss of oxygen chains. The (4 × 1) reconstruction vanishes after Ar-ion-sputtering and subsequent annealing. Additional long sputtering cycles result in a (2 × 1) reconstruction. The observed surface reconstructions can be transformed into each other by heating or sputtering cycles.