In situ scanning tunneling microscopy studies of bimetallic cluster growth: Pt–Rh on TiO2(1 1 0)

The growth of Pt on clusters on TiO2(1 1 0) in the presence and absence of Rh was investigated by scanning tunneling microscopy (STM) for Pt deposited on top of 0.3 ML Rh clusters (Rh + Pt). In situ STM studies of Pt growth at room temperature show that bimetallic clusters are produced when Pt is directly incorporated into existing Rh clusters or when newly nucleated clusters of pure Pt coalesce with existing Rh clusters. Low energy ion scattering experiments demonstrate that Rh is still present at the surface of the clusters even after deposition of 2 ML of Pt, indicating that Rh atoms can diffuse to the cluster surface at room temperature. Rh clusters were found to seed the growth of Pt clusters at room temperature as well as 100 K and 450 K. Furthermore, clusters as large as 100 atoms were observed to be mobile on the surface at room temperature and 450 K, but not at 100 K. Pt deposition at 100 K exhibited more two-dimensional cluster growth and higher cluster densities compared to room temperature experiments due to the lower diffusion rate. Increased diffusion rates at 450 K resulted in more three-dimensional cluster growth and lower densities for pure Pt growth, but cluster densities for Pt + Rh growth were the same as at room temperature.