Structural properties of oxygen on InN(0 0 0 1) surface

First-principles calculations are performed to study the various structures of oxygen (O) adsorbed on InN(0 0 0 1) surfaces. It is found that the formation energy of O on InN(0 0 0 1) decreases with decreasing oxygen coverage. Of all the adsorbate induced surface structures examined, the structure of InN(0 0 0 1)-(2 × 2) as caused by O adsorption at the H3 sites with 0.25 monolayers coverage is most energetically favorable. Meanwhile, nitrogen (N) vacancy can form spontaneously. Oxygen atoms may also substitute N atoms, or accumulate at the voids inside InN film or simply stay on the surface during growth. The oxygen impurity then acts as a potential source for the n-type conductivity of InN as well as the large energy band gap measured.