Surface structure and composition of the missing-row reconstruction of VC0.8(1 1 0): A LEED, GIXRD and photoemission study

Low energy electron diffraction, grazing incidence X-ray diffraction and photoemission were used to decipher the detailed structural arrangement and chemical composition of the surface region of a transition metal carbide, VC0.8(1 1 0). In agreement with previous scanning tunneling microscopy (STM) studies, we find that the surface reconstructs with a ridge-and-valley grating structure along the [ 1 1 ¯ 0 ] direction resulting from {0 0 1} faceting for the (3 × 1) and the (4 × 1) phases. uperstructures terminate on the vacuum side with a nearly stoïchiometric VC region due to C segregation, in contrast with the conclusions drawn from this previous STM study. However, the present experiments clearly show that these phases are metastable, and slow cooling results in a (1 × 1) surface, which is highly C depleted, similarly to the (1 0 0) face.