A novel catalyst of Ni–Mn complex oxides supported on cordierite for catalytic oxidation of toluene at low temperature

The catalytic combustion of toluene over Ni–Mn mixed complex supported on industrial cordierite was investigated. The catalysts were prepared by the wet impregnation method and characterized by using the Brunauer Emmett Teller (BET), Scanning Electron Microscopy (SEM), X-ray diffraction (XRD), Transmission Electron Microscope (TEM) and X-ray fluorescence (XRF). The catalytic activity toward the complete oxidation of toluene to CO2 and H2O strongly depended on the molar ratio of Ni/Mn, loading amount of Ni–Mn oxides, and calcination temperature. All the results above indicated that the Ni–Mn complex oxide catalyst calcined at 400 °C with 0.5 mol ratio of Ni/Mn, 10 wt.% loading amounts, and showed the highest activity as complete oxidation of toluene.