Effect of calcining and Al doping on structure and conductivity of Li7La3Zr2O12
Author/Authors
Chen، نويسنده , , Ru-Jun and Huang، نويسنده , , Mian and Huang، نويسنده , , Wen-Ze and Shen، نويسنده , , Yang and Lin، نويسنده , , Yuan-Hua and Nan، نويسنده , , Ce-Wen، نويسنده ,
Issue Information
هفته نامه با شماره پیاپی سال 2014
Pages
6
From page
7
To page
12
Abstract
Li7La3Zr2O12 (LLZ) ceramics with a garnet-type structure were prepared via the conventional solid-state reaction through different calcining processes. The calcining time and temperature were investigated. The results showed that the ionic conductivity of LLZ samples at room temperature decreased as the calcining temperature increased. The highest conductivity of 2.48 × 10− 4 S cm− 1 was obtained for the sample with the calcining process at 900 °C. The amount of doping Al was also investigated, which showed different effects depending on the calcining process.
Keywords
solid electrolyte , solid-state reaction , Li ion conductivity , Al doping , garnet
Journal title
Solid State Ionics
Serial Year
2014
Journal title
Solid State Ionics
Record number
1712965
Link To Document