Synthesis of poly (1,4-dioxan-2-one) catalyzed by immobilized lipase CA

Polymerization of 1,4-dioxan-2-one was carried out more detailed with immobilized lipase CA as the catalyst. The effect of the enzyme amount, reaction temperature and water content on polymerization was investigated, respectively. Both the conversion of monomer and the Mv of poly(1,4-dioxan-2-one) increased with the increase of enzyme amount, and maximized at 80 °C. At the beginning of polymerization, water molecules act as initiators. As the reaction time increased, linear condensation had gradually became dominant and water was released into the reaction system. Excess water may act as a chain cleavage agent. To obtain poly(1,4-dioxan-2-one) with an ideal molecular weight, polymerization of 1,4-dioxan-2-one was conducted by adding solvent and MS to reaction system, and product with a higher molecular weight (Mv = 58,000) was gained.