Melting and crystallization behavior of poly(trimethylene 2,6-naphthalate)

The melting and crystallization behavior of poly(trimethylene 2,6-naphthalate) (PTN) are investigated by using the conventional DSC, the temperature-modulated DSC (TMDSC), wide angle X-ray diffraction (WAXD) and polarized light microscopy. It is observed that PTN has two polymorphs (α- and β-form) depending upon the crystallization temperature. The α-form crystals develop at the crystallization temperature below 140 °C while β-form crystals develop above 160 °C. Both α- and β-form crystals coexist in the samples crystallized isothermally at the temperature between 140 and 160 °C. When complex multiple melting peaks of PTN are analyzed using the conventional DSC, TMDSC and WAXD, it is found that those arise from the combined mechanism of the existence of different crystal structures, the dual lamellar population, and melting–recrystallization–remelting. The equilibrium melting temperatures of PTN α- and β-form crystals determined by the Hoffman–Weeks method are 197 and 223 °C, respectively. When the spherulitic growth kinetics is analyzed using the Lauritzen–Hoffmann theory of secondary crystallization, the transition temperature of melt crystallization between regime II and III for the β-form crystals is observed at 178 °C. Another transition is observed at 154 °C, where the crystal transformation from α- to β-form occurs.