Radical polymerization of butyl acrylate and random copolymerization of styrene and butyl acrylate and styrene and methyl methacrylate mediated by monospiro- and dispiropiperidinyl-N-oxyl radicals

Radical polymerization of butyl acrylate (BA) and random copolymerizations of styrene (St) and BA and St and methyl methacrylate (MMA) in the presence of 7-aza-15-hydroxydispiro[5.1.5.3]hexadecane-7-yloxyl (1) and 1-aza-2,2-dimethyl-4-hydroxyspiro[5.6]dodecane-1-yloxyl (2) were carried out. Radical polymerization of BA at 120 °C in the presence of 1 gave poly(BA) with Mn=20200 and Mw/Mn=1.30 at 23% conversion. The termination of polymerization observed around ∼20% conversion was solved to a certain extent by an addition of small amounts of dicumyl peroxide, and poly(BA) with Mn=37400 and Mw/Mn=1.33 was obtained in 46% yield. Random copolymerizations of St and BA and St and MMA in the presence of 1 and 2 at 80 °C gave the corresponding random copolymers with narrow polydispersities of 1.12–1.38 at the molar fraction above 0.30 of St in feed. The kinetic study for the NO–C bond homolysis of the corresponding alkoxyamines prepared from 1 and 2 were carried out, and evaluation of the preexponential factors (Aact) and the activation parameters (Eact) showed that the steric factors of the nitroxides are reflected mainly on Eact.