Synthesis, characterization and thermal properties of soluble aromatic poly(amide imide)s

Novel diamines such as N,N′-bis(aminoaryl)terephthalamido-2-carboxylic acids (BATCA), which contain primary amine, amide and carboxylic acid groups and are soluble in dilute aqueous NaOH solution, were synthesized by reacting aromatic diamines with trimellitic anhydride chloride in dimethylformamide. Poly(amide imide)s containing 3:1 ratio of amide:imide groups in the polymer chain were prepared by low temperature solution polymerization of BATCAs with isophthaloyl chloride or terephthaloyl chloride in dimethylformamide at 5–10 °C to form poly(amide amic acid)s, and followed by treating with a mixture of triethylamine and acetic anhydride. The PAIs were soluble in polar aprotic solvents like dimethylformamide, dimethylacetamide, dimethylsulphoxide and N-methylpyrrolidone, and have inherent viscosities in the range of 0.30–0.66 dL/g. The PAIs were characterized by IR, 1H NMR and 13C NMR techniques. Thermogravimetric analysis (TGA) has shown that the initial decomposition temperatures of the polymers are in the range of 250–440 °C, depending upon the structures of diamine and diacid chloride. The glass transition temperatures of the PAIs are in the range of 128–320 °C. The IDT and Tg values of the polymers containing terephthaloyl unit are higher by about 20–40 °C than those of the polymers with isophthaloyl unit. BATCA could be utilized for the preparation of thin film composite membranes having PAA/PAI barrier layer on PES by in situ interfacial polymerization with IPC/TPC/TMC.