Polymer-layered silicate nanocomposites prepared through in situ reversible addition–fragmentation chain transfer (RAFT) polymerization

Reversible addition–fragmentation chain transfer (RAFT) polymerizations were performed in the presence of organically modified clays and successfully prepared polystyrene-, poly(methyl methacrylate)-, and poly(n-butyl acrylate)-layered silicate nanocomposites. The polymers had well-defined molecular weights and low polydispersities, as expected from RAFT polymerizations. The morphology of polystyrene-, and poly(n-butyl acrylate)-nanocomposites were found to be exfoliated using montmorillonite modified with N,N-dimethyl-n-hexadecyl-(4-vinylbenzyl) ammonium (MMT-VB16). In the case of PMMA nanocomposite, the structure was a mixture of intercalated and exfoliated when MMT-VB16 was used, while the use of montmorillonite modified with 2-methacryloyloxyethyl-hexadecyldimethyl ammonium (MMT-MA16) resulted in exfoliation.