Synthesis and properties of sulfonated copoly(p-phenylene)s containing aliphatic alkyl pendant for fuel cell applications

A series of novel copoly(p-phenylene)s (PPs) containing an alkyl pendant were successfully synthesized via Ni(0)-catalyzed coupling polymerization. Sulfonated copolymers (SPPs) were achieved by postsulfonation from concentrated H2SO4. SPPs showed good solubility in polar aprotic solvents and gave flexible, tough, and transparent free-standing films by solvent casting. The ion exchange capacities (IECs) of the membranes ranged from 2.50 to 2.65 meq/g. All SPP membranes displayed proton conductivity similar to or higher than that of Nafion, especially at high relative humidity (>70% RH) (SPP-1: 0.271 Scm−1, SPP-2: 0.284 Scm−1, SPP-3: 0.212 S cm−1, Nafion: 0.127 Scm−1; at 80 °C and 95% RH). They also exhibited acceptable water uptake in the range of 52–56 vol% at 80 °C with little dimensional change. The gas permeability of the SPP membranes was much lower than that of Nafion 112. Therefore, these materials are promising for fuel cell application.