Functionalization of shaped polymeric nanoobjects via bulk co-self-assembling gelable block copolymers with silane coupling agents

Hairy polymer nanoobjects (PNOs) of different shapes can be easily obtained by cross-linking the discontinuous microphases of bulk block copolymers followed by dispersing in a solvent. Herein we report a general approach to functionalize the shaped PNOs by bulk microphase separation of poly(3-(triethoxysilyl)propyl methacrylate)-block-polystyrene (PTEPM-b-PS) copolymers in the presence of functional silane coupling agents. The silanes like (3-mercaptopropyl)trimethoxysilane and (3-chloropropyl)trimethoxysilane were enriched into the PTEPM discontinuous microdomains selectively. The microphase structures were characterized by small angle X-ray scattering (SAXS) and transmission electron microscopy (TEM) of microtomed slices. For the PTEPM78-b-PS348 which had a lamellar structure, its blending mixtures with MMS and CMS whose content reached up to 50 wt% still remained as a lamellar structure. When small amount of MMS or CMS was added, the PTEPM71-b-PS780 as hexagonally packed cylinders remained its structure. However, the morphology changed into lamellae at higher content of the silanes. For PTEPM46-b-PS1669, its spherical structure remained but the size distribution became broad gradually with increase of silanes. By inducing gelation and then dispersing in a good solvent of PS phases, hairy PNOs having lamellar, cylindrical or spherical shape with their cores being functionalized with the groups from co-gelated silanes were obtained.