EPR observation of first point defects in cubic boron nitride crystalline powders

An X-band electron paramagnetic resonance (EPR) study of nominally pure, diamond-like cubic boron nitride (c-BN) crystalline powders, has led to the first identification of a spectrum attributed to two related paramagnetic species. The composite EPR spectrum can be observed only in dark brown colored powders known to contain excess of boron. It consists of two superimposed lorentzian components, called D1 and D2, centered at g1=2.0063 and g2=2.0084, with peak-to-peak linewidths of 3.3 and 17.9 mT, respectively. The temperature dependence of the integrated intensities, their linewidths and intensity ratio D2/D1 allows one to conclude that the narrow line D1 originates from EPR transitions inside a S=1/2 ground doublet and the broad line D2 from transitions inside the excited levels of another center. Evidence suggests that both centers are boron related paramagnetic species.