Nonlinear optical properties of silver colloidal solution by in situ synthesis technique

The silver colloidal solutions were prepared by in situ synthesis technique in the presence of the Polymethyl Methacrylate, which was polymerized by reversible addition-fragmentation transfer. The UV–VIS spectra and transmission electron microscopy had shown the formation of sphere silver nanoparticles with average size of 10 nm. Nonlinear optical properties as a function of silver concentration were studied using Z-scan technique with 13 ns pulse duration at 532 nm. The optical nonlinearity enhancement was observed by increasing the concentration. The third-order nonlinear susceptibility χ(3) was measured to 1.045 × 10−11 esu when the concentration was 2.13 mg/ml. Besides, the sample was founded to exhibit a shift from saturable absorption to reverse saturable absorption at higher incident laser energy. The reverse saturable absorption was observed to be responsible for the optical limiting characteristics in our experiments.