Influence of WC addition in Co–Cr–W–Ni–C flame sprayed coatings on microstructure, microhardness and wear behaviour

In present paper the influence of the tungsten carbide (WC) particle addition on the microstructure, microhardness and abrasive wear behaviour of flame sprayed Co–Cr–W–Ni–C (EWAC 1006) coatings deposited on low carbon steel substrate has been reported. Coatings were deposited by oxy-acetylene flame spraying process. Wear behaviour of coatings was evaluated using pin on flat wear system against SiC abrasive medium. It was observed that the addition of WC particle in a commercial Co–Cr–W–Ni–C powder coating increases microhardness and wear resistance. Wear behaviour of these coatings is governed by the material parameters such as microstructure, hardness of coating and test parameters (abrasive grit size and normal load). Addition of WC in a commercial powder coating increased wear resistance about 4–9 folds. WC modified powder coatings showed better wear resistance at high load. Heat treatment of the unmodified powder coatings improved abrasive wear resistance while that of modified powder coating deteriorated the wear resistance. SEM study showed that wear of coatings largely takes place by microgroove, crater formation and scoring. Electron probe micro analysis (E.P.M.A.) of unmodified and WC modified powder coating was carried out for composition and phase analysis.