Thermo-physical and thermal cycling properties of plasma-sprayed BaLa2Ti3O10 coating as potential thermal barrier materials

Increased turbine inlet temperature in advanced turbines has promoted the development of thermal barrier coating (TBC) materials with high-temperature capability. In this paper, BaLa2Ti3O10 (BLT) was produced by solid-state reaction of BaCO3, TiO2 and La2O3 at 1500 °C for 48 h. BLT showed phase stability between room temperature and 1400 °C. BLT revealed a linearly increasing thermal expansion coefficient with increasing temperature up to 1200 °C and the coefficients of thermal expansion (CTEs) are in the range of 1 × 10− 5–12.5 × 10− 6 K− 1, which are comparable to those of 7YSZ. BLT coatings with stoichiometric composition were produced by atmospheric plasma spraying. The coating contained segmentation cracks and had a porosity of around 13%. The microhardness for the BLT coating is 3.9–4.5 GPa. The thermo-physical properties of the sprayed coating were investigated. The thermal conductivity at 1200 °C is about 0.7 W/mK, exhibiting a very promising potential in improving the thermal insulation property of TBC. Thermal cycling result showed that the BLT TBC had a lifetime of more than 1100 cycles of about 200 h at 1100 °C. The failure of the coating occurred by cracking at the thermally grown oxide (TGO) layer due to severe oxidation of bond coat. Based on the above merits, BLT could be considered as a promising material for TBC applications.