Temperature influence on structural changes of foundry bentonites

The results of investigations of three calcium bentonites, activated by sodium carbonate, applied in the foundry industry as binding material for moulding sands, subjected to the influence of high temperatures – are presented in the paper. Investigations were performed by the thermal analysis (TG) method, the infrared spectroscopy (FTIR) method and the modern Cu(II)–TET complex method (used for the determination of the montmorillonite content in bentonite samples). The occurrence of the dehydration process and two-stage dehydroxylation process was confirmed only for bentonite no. 2. This probably indicates that cis- and trans-isomers are present in the octahedric bentonite structure. Tests were performed at temperatures: 500, 550, 700, 900, 1000, 1100, 1200 °C.