Evaluation of water transfer from saturated lightweight aggregate to cement paste matrix by neutron radiography

In high-strength concrete with low water–cement ratio, self-desiccation occurs due to cement hydration and causes shrinkage and an increased risk of cracking. While high-strength concrete has a denser matrix than normal-strength concrete, resulting in lower permeability, early-age cracks would cancel out this advantage. For the mitigation of this self-desiccation and resultant shrinkage, water-saturated porous aggregate, such as artificial lightweight aggregate, may be used in high-strength concrete. In this contribution, for the purpose of clarification of the volume change of high-strength concrete containing water-saturated lightweight aggregate, water transfer from the lightweight aggregate to cement paste matrix is visualized by neutron radiography. As a result, it is clear that water was supplied to the cement paste matrix in the range 3–8 mm from the surface of the aggregate, and the osmotic forces may yield water transfer around lightweight aggregate in a few hours after mixing.