Microstructure of spray converted nanostructured tungsten carbide-cobalt composite

This paper reports the presence of face centered cubic cobalt precipitates inside tungsten carbide in nanocomposite of WC-Co synthesized by spray conversion processing. EDS was used to identify the presence and micro-diffraction was employed to determine the nature of the precipitates. There is entrapment of cobalt in tungsten carbide during the spray conversion process used to form WC/Co powder. During consolidation, at high temperatures, the cobalt attains enough mobility to precipitate inside WC. A vanadium containing compound was seen at the interfaces in samples which incorporated VC as a grain growth inhibitor.