Effects of crystalline particles on mechanical properties of strip-cast Zr-base bulk amorphous alloy

Effects of crystalline phase particles formed in a strip-cast Zr-base bulk amorphous alloy on strength, ductility, and fracture toughness were investigated by directly observing microfracture processes using an in situ loading stage installed inside a scanning electron microscope chamber. The compressive and fracture toughness test results indicated that strength, ductility, and fracture toughness of the strip-cast amorphous alloy were higher than those of the as-cast monolithic amorphous alloy, although the strip-cast alloy contained a considerable amount (4.5 vol.%) of hard, brittle crystalline particles. According to the in situ microfracture observation, crystalline particles were easily cracked under low stress levels, acted as blocking sites of shear band or crack propagation, and provided initiation sites of multiple shear bands. Thus, the improvement of mechanical properties in the strip-cast alloy could be explained by mechanisms of (1) blocking of crack propagation, (2) formation of multiple shear bands, and (3) crack deflection by crystalline particles.