Low-temperature synthesis of metal tungstates nanocrystallites in ethylene glycol

In this paper, we report the low-temperature synthesis of metal tungstate, MWO4 (M=Ca, Sr, Ba, Cd, Zn, Pb) nanocrystallites. By reaction between metal chloride and sodium tungstate in ethylene glycol at 180 °C for 10 h, well-crystallized tungstate particles were successfully obtained. Characterization by X-ray powder diffraction (XRD) and transmission electron microscopy (TEM) shows that the product powders consist of nanosize particles. Photoluminescence measurement reveals that the as-obtained CaWO4, CdWO4, and PbWO4 show excitonic peaks at about 430, 500 and 500 nm, respectively. The solvent and reaction conditions are important in the formation of the products.