Effect of Cu/In molar ratio on the microstructural and optical properties of microcrystalline CuInS2 prepared by solvothermal route

Synthesis and characterization of CuInS2 powder sample prepared by a simple and convenient solvothermal method is reported. The influence of the variation of Cu/In molar ratio from 0.69 to 1.25 on the particle morphology, crystal structure and optical properties of CuInS2 samples was studied. The X-ray diffraction studies indicated that the samples were polycrystalline in nature. SEM images of the samples revealed that the copper-rich products were uniform microspheres with smooth surfaces, whereas microspheres formed by network of interconnected flakes were obtained for indium-rich products. The optical band gaps (Eg) of the products decreased from 1.60 to 1.43 eV with variation of Cu/In molar ratio. The variation of the Urbach tail width with Cu/In molar ratio indicated that the density of the defects is much higher for the indium-rich CuInS2, which was clearly revealed from Raman measurements.