Hydrothermal synthesis of composites of well-crystallized hydroxyapatite and poly(vinyl alcohol) hydrogel

Composites of hydroxyapatite (HAp) and poly(vinyl alcohol) (PVA) hydrogel were fabricated by the hydrothermal treatment of calcium phosphate powder. Alpha-tricalcium phosphate (α-TCP) or beta-tricalcium phosphate (β-TCP) powder was dispersed in PVA hydrogel and exposed to water vapor at 120 °C, 140 °C or 160 °C for 6 h. Low crystallinity HAp was formed in specimens prepared from α-TCP and PVA hydrogel prior to hydrothermal treatment, which was caused by hydrolysis of α-TCP. This allowed specimen shape to be retained after hydrothermal treatment. β-TCP showed less reactivity in forming HAp in the PVA hydrogel, which led to the formation of large rod-shaped crystals approximately 15 μm in length. Specimens from β-TCP and PVA were too soft to retain their shape after hydrothermal treatment. HAp with controlled morphology was prepared using different types of tricalcium phosphate precursor. The application of α-TCP allowed the in situ fabrication of HAp/PVA composites.